Abstract
Stationary sorbents play a key role in the separation process. We present here a kind of unique separative material, called thiophilic affinity MOFs, as specific sorbent for the capture of compounds containing disulfide-bond. The sorbent was obtained through epoxide ring-opening reaction among MOF-5-NH2, tris(2,3-epoxypropyl) isocyanurate, and thiophilic reagents under mild reaction condition. The synthesized sorbent was characterized with X-ray diffraction, scanning electron microscope, transmission electron microscope, Fourier transform infrared, thermogravimetric analysis and N2 absorption. The capillary electrophoresis experiments verified their high specific recognization and separation for disulfide bond-containing compounds.
Similar content being viewed by others
1 Introduction
Metal organic frameworks (MOFs) were generated by the polymerization reaction of organic linker and inorganic metal clusters to form 3D porous materials [1, 2]. Compared with other inorganic porous materials, MOFs have some unique characteristics, which make them have great potential for the separation. Firstly, fascinating surface areas can meet the requirement for normal stationary sorbents perfectly. Secondly, good thermal stability make it can be used in severe experiment condition; Thirdly multifarious organic linker make it have different functional surface. [3,4,5,6,7,8]. However, the exploration of MOFs as efficient sorbents for the separation of liquid sample are relatively lagged behind. There are two main reasons: (1) some MOFs will lose its stability in polar solvent so that they only can use a single nonpolar or low polar solvent [9]; (2) specific liquid separation beyond the adsorption-based mechanism is a challenge for long time [10, 11]. Therefore, it is urgent and imperative to develop a stable and effective MOFs based materials for the specific liquid separation.
The superamolecular metallopolymer and polymer-MOF hybrid materials was proposed by Cohen et al. [12, 13] Supermaolecular metallopolymer can formed ‘soft’ organic building block connecting by metal ions, when the organic polymer linker and metal ions is changed, and their physicochemical properties would change, too. The polymer-MOF hybrid materials integrate organic polymer into the MOF lattice because the polymers have necessary mulitopic ligands for MOF formation. It can exhibit properties of MOFs such as high porosity and crystallinty, as well as polymer properties such as high stability. The integrated properties of hybrid materials will expand application of MOF [14,15,16,17,18].
It is well-known that sulfone is attractive as affinity ligand for many applications, such as probe, self-assembly and separation [19]. Sulfone can covalently react with disulfide bond to form esters in high concentration salt solution and dissociate in low concentration. This association between thiophilic sorbents and disulfide bond-containing compounds was discovered firstly by Porath et al. [20], and the thiophilic affinity chromatogrphy (TAC) method was found. Nowadays, extensive attention have been paid to thiophlic affinity adsorbents. Thamarapu et al. used thiophilic interaction chromatography to separate transferrins in serum, which may provide a sample and efficient method to monitor levels of transferrins for monitoring the progress of Alzheimer’s disease [21]. What’s more, Elzbie displayed a thiophilic interaction (3S, T-gel) chromatography methodology to isolate various PSA molecular forms present in biological fluids [22]. High quality separation material should be charaterized by high stength and easy surface modification. However, the most existing thiophlic chrmatographic materials are based on soft substrate such as gel [23] or fiber [24]. They have poor mechanical strength and difficult to storage.
The MOFs materials synthesized by polymerization have high mechanical strength and high stability. In this article, a novel unique thiophilic affinity MOFs were designed and synthesized based on copolymerization reaction among the MOF-5-NH2 derivatives, tris(2,3-epoxypropyl) isocyanurate (TEPIC) and sulfamide (SFA). The MOF-5-NH2 can assemble with TEPIC and SFA spontaneously in solution. The prepared polymer-MOF hybrid thiophilic affinity material were competent to specifically recognize and enrich the disulfide bond-containing compounds.
2 Experimental section
2.1 Materials
The thiophilic regents sulfamide (SFA) was purchased from Aladdin and its chemical structure were shown in Fig. 1. Zn(NO3)2·6H2O, and tris(2,3-epoxypropyl) isocyanurate (TEPIC) also were purchased from Aladdin (Shanghai, China). 2-aminoterephthalic acid was purchased from Ark Pharm (Shanghai, China). N,N-dimethylformamide (DMF), dimethyl sulfoxide (DMSO), acetonitrile (ACN), methanol and ethanol were obtained from Sinopharm Chemical Reagent (Shanghai, China). Bis(4-hydroxyphenyl) disulfide (2S-OH) and 4,4′-(dihydroxyphenyl) methane (2-OH) were purchased separately from TCI (Shanghai, China) and Aladdin (Shanghai, China).
All chemicals and reagents were at least of analytical grade. Ultrapure water (18.2 MΩ cm) was obtained from a water purification system (PSDK2-10-C, Beijing city, China).
Standard solution of bis(4-hydroxyphenyl) disulfide (2S-OH) (0.1 mg mL−1) and bis 4, 4′-Dihydroxydiphenyl methane (2-OH) (0.1 mg mL−1) were prepared with acetonitrile. The loading buffer (pH = 6.2) was composed of KCl (3.727 g, 0.50 mol L−1) and Na2HPO4 (1.433 g, 0.04 mol L−1), with ultrapure water dissolved and transferred into 100 mL volumetric flask. The preparation of eluent (pH = 6.2) with Na2HPO4 (1.433 g, 0.04 mol L−1) was same as above. The two kinds of solution were used for immobilized and elution of sample. The background buffer solution was prepared with Na2HPO4 (0.895 g, 0.05 mol L−1, pH = 8.5). All of the above buffer solution were prepared with sodium citrate regulating pH to designated value and were reserved in refrigerator for CE.
2.2 Preparation of thiophilic affinity MOFs
The matrix MOF-5-NH2 was prepared by the method of literature and partly improved [25]: Zn(NO3)2·6H2O (0.595 g, 2.0 mmol) were dispersed in 50 mL DMF in a three-necked flask. Subsequently, 2-amino terephthalic acid (0.181 g, 1.0 mmol) was added into the above mixed solution and the polymerization was kept for 2 h under stirring at 140 °C. Then, the solid precipitates were collected and washed thoroughly with DMF, ethanol for three times, respectively. When the unreacted substance was removed, the prepared MOF-5 -NH2 was dried at 50 °C in the drying oven for 12 h.
Afterwards, the above MOF-5-NH2 (0.310 g, 0.4 mmol) as matrix, TEPIC (0.119 g, 0.4 mmol) as the crosslinker, SFA (0.038 g, 0.4 mmol) as functional monomer were well-blended in the 50 mL DMSO. Then the system was kept stirring for 12 h at 75 °C. The MOF-5-NH2@P(TEPIC-co-SFA) was synthesized based on the ring opening reaction of expoxy group. At last, the resulting sorbent was collected, followed by rinsed with methanol for three times before drying at 50 °C overnight for future use. An illustration of the preparation of MOF-5-NH2@P(TEPIC-co-SFA) was presented in Fig. 1.
2.3 Characterization
Scanning electron microscopy (SEM, Hitachi S-4800, Japan) was performed at 5 kV. Transmission electron microscopy (TEM, Hitachi HT-7700, Japan) was performed at 100 kV. The X-ray diffraction (XRD, Bruker D8 Advance, German) patterns were recorded using Cu/Kα radiation at 40 kV and 40 mA. Fourier transform infrared spectrometer (FT-IR-21, Shimadzu, Japan) spectra were recorded from 4000 to 50 cm−1. Thermogravimetric analyses (TGA, DTG-60A, Japan) was performed under air atmosphere. The heating rate was 10 °C min−1 and the hold temperature was set to 800 °C. The specific surface area and porous behavior (BET, JW-BK112 JWGB SCI&TECH, China) were measured by N2 adsorption and desorption at 77 K. The sample detection was carried out by capillary electrophoresis (CE) apparatus (P/ACE™ MDQ, Beckman, USA).
3 Results and discussion
3.1 Characterization
3.1.1 SEM and TEM of MOF-5-NH2@P(TEPIC-co-SFA)
MOF-5 is an important archetype metal–organic framework which oxocentered Zn4 tetrahedra are connected with linear organodicarboxylates to produce a cubic network structure [26,27,28]. Due to its high specific area surface and controlled pore size, it has been studied in the separation technology [29]. But its organic unit are mainly composed of nonpolar functional group, according to the literature [29]. Some MOFs may degrade in the polar solvent, such as H2O and CH3CN, CH3OH. Therefore, the hydrophilic amino (–NH2) group was tentatively introduced into MOF-5. In this paper, we chose MOF-5-NH2, TEPIC and SFA as matrix, crosslinker, and functional monomers, respectively. The sulfone group was modified on the MOF through the epoxy ring opening reaction, and a polymer-MOF hybrids MOF-5-NH2@P(TEPIC-co-SFA) was obtained, and it was severed as the affinity thiophilic sorbentin in the separated experiments.
The reaction temperature was found to be a key factor for the preparation of the affinity thiophilic sorbents. When the temperature was lower than 75 °C, the thiophilic affinity sorbent MOF-5-NH2@P(TEPIC-co-SFA) was not well formed; when the temperature was higher than 75 °C, the porous of the thiophilic affinity sorbent become dense, and even disappeared (Fig. 2), which would affect its separation ability. The reaction time was also crucial to synthesize the sorbent. No matter the time was above 12 h or below the 12 h, the morphology of the sorbent was not intact (Fig. 3). Based on the above results, the optimal reaction condition was kept at 75 °C for 12 h. The obtained product was brown powder. The sorbent is nearly cubic with well-controlled skeletal and well distributed porous. TEM images (Fig. 4) further proved the sorbent is dispersed uniformly.
3.1.2 XRD, FT-IR measurements
The XRD patterns of MOF-5-NH2 and MOF-5-NH2@P(TEPIC-co-SFA) were shown in Fig. 5. MOFs-5-NH2 exhibited well-defined diffraction peaks. The diffraction peaks at 2θ = 7.76°(200), 9.74°(220), 13.94°(400) were attributed to the characteristic reflection of MOF-5-NH2 which were in accordance with the results in the literature [30]. However, the intensity of the synthesized MOF-5-NH2@P(TEPIC-co-SFA) decreased apparently, which was attributed to the distortion of the MOF-5-NH2 crystal structure after combination with TEPIC-co-SFA.
Fourier transform infrared (FT-IR) spectroscopy was used to detect the homologous infrared absorption characteristic peaks of the sorbent. As we can see from Fig. 6a, MOF-5-NH2 has two apparent stretching vibration at 3286 cm−1 and 3155 cm−1, which approved the vibration of N–H, but they were disappeared in MOF-5-NH2@P(TEPIC-co-SFA) (Fig. 6c). It means that the amido of MOF-5-NH2 has coordinated with epoxy group. Due to the polymerization between SFA (Fig. 6b) and TEPIC, the characteristic stretching vibration of –S=O of SFA slight blue shift from 1350 cm−1 and 1156 cm−1 to 1309 cm−1 and 1219 cm−1, which is consistent with the literature [31]. Peaks at 1600,1500 and 1390 cm−1 was related with the C=O symmetric and asymmetric vibration in the carboxyl group (R-COO–) of the secondary unit (Zn4O6+), which was from 2-amino terephthalic acid. Absorptive peaks of aromatic skeletal stretching vibration were at 1500 and 1600 cm−1. All these results confirm the presence of sulfone group in the sorbent.
3.1.3 TGA, BET measurements
The thermal stability of affinity thiophilic sorbent was characterized by the thermalgravimmetric analysis (TGA) in air atmosphere. As we can see from Fig. 7, the weight loss of MOF-5-NH2@P(TEPIC-co-SFA) is a three-steps process. A weight loss of about 12% was observed before 125 °C,which could be owing to the residual solvent molecule in the porous structure. The moisture in the surface and channels with weight loss of only 5% is observed between 125 and 310 °C. The decomposition of MOF-5-NH2@P(TEPIC-co-SFA) is detected at about 310 °C, which indicates that the obtained sample has excellent thermal stability. The major weight loss of MOF-5-NH2@P(TEPIC-co-SFA) sample is detected between 310 and 525 °C. The skeleton of MOF-5-NH2@P(TEPIC-co-SFA) is destroyed completely when the temperature reach at 525 °C. The degradation temperature was similar to that of MOF-5, which meant that the affinity thiophilic material has good thermal stability.
The modest surface area for separated sorbent in chromatography was 200–800 m2 g−1 and the pore size in the range of 2–25 nm [32]. From the N2 adsorption–desorption isotherm in Fig. 8, the average pore size of MOF-5-NH2@P(TEPIC-co-SFA) was 15.58 nm and the surface area 248.14 m2 g−1 As for MOF-5-NH2, the data is 15.83 nm and 81.77 m2 g−1. The pore size is retained after hybridation, however, the surface area was increased threefold, which make the obtained sample has a suitable surface condition for sorbent. In addition, as a functional monomer, SFA provide hydrophilic group, including sulfonyl group (O=S=O) and amino group (–NH2), which made the sorbent possessed hydrophilicity. The prepared polymer-MOF hybrid material was more suitable for liquid separation.
3.2 Thiophilic affinity
3.2.1 Experimental conditions of capillary electrophoresis
All capillary electrophoresis data were obtained from capillary electrophoresis apparatus. A new fused silica capillary column with total length up to 50 cm was put into use. The detection wavelength was set at 214 nm. The separated voltage was 15 kV. Before each injection, the column was rinsed by 0.1 mol L−1 NaOH, 0.1 mol L−1 HCl, ultrapure H2O and 0.05 mol L−1 background buffer solution in sequence under the pressure of 20 psi. The condition of sample injection was 0.5 psi × 8 s.
3.2.2 Adsorption of compounds containing disulfide-bond
The whole procedure for specific enrichment and separation of compounds containing disulfide-bond includes three steps: immobilized, washing, and elution (Fig. 9). Firstly, 10 mg thiophilic affinity absorbent was put into a 1.5 mL centrifuge tube, and 600 μL loading buffer and 800 μL mixed standard solution were added. In order to immobilize the disulfide bond-containing compound on the sorbent, the mixture was sufficient vibrated for 20 min, and then the supernatant liquid was discarded after centrifugation. Subsequently, 300 μL loading buffer was added and repeated the operation of sufficient fixation for twice. Finally, the supernatant liquid was collected for capillary electrophoresis analysis after 15 μL eluent was added and vibrated for 10 min.
On the basis of the separation mechanism of thiophilic affinity chromatography, we demonstrate the feasibility of the affinity sorbent for specific capture of compound containing disulfide-bond, with bis(4-hydroxyphenyl) disulfide and 4, 4′-Dihydroxydiphenyl methane as the test compounds (Fig. 10). The difference between bis(4-hydroxyphenyl) disulfide and 4,4′-dihydroxydiphenyl methane was that one has disulfide bond and the other has no disulfide bond. From Fig. 11, it can be seen that the captured bis(4-hydroxyphenyl) disulfide has a sharper peak, its peak area was 20 times than that of initial standard sample. It meant that the bis(4-hydroxyphenyl) disulfide was enriched. As a contrast, 4, 4′-Dihydroxydiphenyl methane, which has no disulfide bond, didn’t display any CE signal under the same detection condition. The results demonstrated MOF-5-NH2@P(TEPIC-co-SFA) had apparent affinity to disulfide bond-containing compound.
Additionally, the affinity separation capacity of MOF-5-NH2@P(TEPIC-co-SFA) was further investigated with the solution of 2S-OH (0.1 mg mL−1) through the whole separation process, including the sample loading, washing and elution operations. The relative standard deviation of CE signal for run to run was about 41.92%, and batch to batch was about 28.07%.
4 Conclusions
In this paper, a method for preparation of thiophilic affinity sorbent was proposed through combing the MOF with polymer. The designed and synthesized sorbent can specifically capture disulfide bond-containing compounds. Especially, the hydrophilic functional monomer facilitates its application in the water system. Because of the widespread presence of compounds containing disulfide-bond in nature, such as, proteins, antibody. The application of MOFs will be well designed and functionalized to make the thiophilic affinity sorbents a promising material in the near future.
References
Eddaoudi M, Li H, Yaghi OM (2000) Highly porous and stable metal–organic frameworks: structure design and sorption properties. J Am Chem Soc 122:1391–1397
Zhu YL, Zhou XH, Li L, You YJ, Huang W (2017) A water-stable metal-organic framework as a luminescent Fe3+ sensor under weak acidic and weak basic conditions. Sci China Chem 60:1581–1587
Gao J, Huang CH, Lin YF, Tong P, Zhang L (2019) In situ solvothermal synthesis of metal-organic framework coated fiber for highly sensitive solid-phase microextraction of polycyclic aromatic hydrocarbons. Chem Eng J 365:40–50
Ranjbar M, Taher MA (2016) Preparation of Ni-metal organic framework-74 nanospheres by hydrothermal method for SO2 gas adsorption. J Porous Mater 23:1249–1254
Liu YL, Gao PF, Huang CZ, Li YF (2015) Shape- and size-dependent catalysis activities of iron-terephthalic acid metal-organic frameworks. Sci China Chem 58:1553–1560
Zeng PY, Li JW, Ye M, Zhuo KF, Fang Z (2017) In situ formation of Co9S8/N-C hollow nanospheres by pyrolysis and sulfurization of ZIF-67 for high-performance lithium-ion batteries. Chem Eur J 40:9517–9524
Zhao YY, Wang WW, Chen MN, Wang RJ, Fang Z (2017) The synthesis of ZnS@MoS2 hollow polyhedrons for enhanced lithium storage performance. CrystEngComm 20:7266–7274
Priscilla RB, Idaira PF, Jorge P, Pino V (2016) Are metal-organic frameworks able to provide a new generation of solid-phase microextraction coatings? A review. Anal Chim Acta 939:26–41
Yusuf K, Aqel A, ALOthman Z (2014) Metal–organic frameworks in chromatography. J Chromatogr A 1348:1–16
Li PZ, Su J, Liu J, Liang J, Zhang YY, Chen HZ, Zhao YL (2017) A highly porous metal–organic framework for large molecule capture and chromatographic separation. Chem Commun 53:3434–3437
Huang K (2015) A ZIF-71 hollow fiber membrane fabricated by contra-diffusion. ACS Appl Mater Interfaces 7:16157–16160
Bentz KC, Cohen SM (2018) Supramolecular metallopolymers: from linear materials to infinite networks. Angew Chem Int Ed 57:14992–15001
Ayala S, Bentz KC, Cohen SM (2019) Block co-polyMOFs: morphology control of polymer–MOF hybrid materials. Chem Sci 10:1746–1753
Palomba JM, Credille CV, Kalaj M, DeCoste JB, Peterson GW, Tovar TM, Cohen SM (2018) High-throughput screening of solid-state catalysts for nerve agent degradation. Chem Commun 54:5768–5771
Denny MS, Moreton JC, Benz L, Cohen SM (2016) Metal–organic frameworks for membrane-based separations. Nat Rev Mater 1:1–17
Zhang YY, Feng X, Li HW, Chen YF, Zhao JS, Wang L, Wang S, Wang B (2015) Photoinduced postsynthetic polymerization of a metal–organic framework toward a flexible stand-alone membrane. Angew Chem Int Ed 54:4259–4263
Marti A, Tran D, Balkus KJ (2015) Fabrication of a substituted imidazolate material 1 (SIM-1) membrane using post synthetic modification (PSM) for pervaporation of water/ethanol mixtures. J Porous Mater 22:1275–1284
Yao BJ, Jiang WL, Dong Y, Liu ZX, Dong YB (2016) Post-synthetic polymerization of UiO-66-NH2 nanoparticles and polyurethane oligomer toward stand-alone membranes for dye removal and separation. Chem Eur J 22:10565–10571
Qian H, Lin ZY, Xu HM, Chen MQ (2009) The efficient and specific isolation of the antibodies from human serum by thiophilic paramagnetic polymer nanospheres. Biotechnol Progr 25:376–383
Porath J, Maisano F, Belew M (1985) Thiophilic adsorption—a new method for protein fractionation. FEBS Lett 185:306–310
Srikrishnan T, MacKenzie JT, Sulkowski E (2006) Thiophilic interaction chromatography of human transferrins. J Chromatogr Sci 44:634–638
Kawinski E, Levine E, Chadha K (2002) Thiophilic interaction chromatography facilitates detection of various molecular complexes of prostate-specific antigen in biological fluids. Prostate 50:145–153
Salgado FJ, Vazquez S, Iglesias A, Perez DA, Mera VA, Arias P, Nogueira M (2010) Application of thiophilic chromatography to deplete serum immunoglobulins in sample preparation for bidimensional electrophoresis. Anal Chim Acta 658:18–31
Zhang SH, Yang Q, Yang XM, Wang WC, Li Z, Zhang LH, Wang C, Wang Z (2017) A zeolitic imidazolate framework based nanoporous carbon as a novel fiber coating for solid-phase microextraction of pyrethroid pesticides. Talanta 166:46–53
Cendrowski K, Skumial P, Spera P, Mijowska E (2016) Thermally induced formation of zinc oxide nanostructures with tailoring morphology during metal organic framework (MOF-5) carbonization process. Mater Des 110:740–748
Greer HF, Liu YH, Greenaway A, Wright PA, Zhou WZ (2016) Synthesis and formation mechanism of textured MOF-5. Cryst Growth Des 16:2104–2111
Chen B, Wang XJ, Zhang QF, Xi XY, Cai JJ, Qi H, Shi S, Wang J, Yuan D, Fang M (2010) Synthesis and characterization of the interpenetrated MOF-5. J Mater Chem 20:3758–3767
Kaye SS, Dailly A, Yaghi OM, Long JR (2007) Impact of preparation and pandling on the hydrogen storage properties of Zn4O(1,4-benzenedicarboxylate)3(MOF-5). J Am Chem Soc 129:14176–14177
Yaghi OM, Keeffe MO, Ockwig NW, Chae HK, Eddaoudi M, Kim J (2003) Reticular synthesis and the design of new materials. Nature 423:705–714
Zhu LJ, Jia XY, Bian H, Huo T, Duan ZB, Xiang YZ, Xia DH (2018) Structure and adsorptive desulfurization performance of the composite material MOF-5@AC. New J Chem 42:3840–3850
Liu YC, Ren LB, Liu Z (2011) A unique boronic acid functionalized monolithic capillary for specific capture, capture, separation and immobilization of cis-diol biomolecules. Chem Commun 47:5067–5069
Ahmad R, Wongfoy AG, Matzger AJ (2009) Microporous coodination polymers as selective sorbents for liquid chromatography. Langmuir 25:11977–11979
Acknowledgements
We gratefully acknowledge the “National Natural Science Foundation of China” (Grant No. 21405003), and Open fund of “Beijing Key Laboratory of Detection Technology and Quality Evaluation of Organic Material” (Grant No. 201501003) for financial support.
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflict of interest
The authors declare that they have no conflict of interest.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
About this article
Cite this article
Wen, Q., Sun, T., Wang, Q. et al. Unique thiophilic affinity MOFs as specific sorbent for disulfide bond-containing compounds capture. SN Appl. Sci. 1, 747 (2019). https://doi.org/10.1007/s42452-019-0799-3
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s42452-019-0799-3